PA6-X028 by BASF

HIGH PERFORMANCE MATERIAL

The PA6-X028 3D material by BASF offers new possibilities for the series production of high performance functional parts requiring high accuracy, strength and thermal distortion stabililty for 3D printing in automotive and in other industrial sectors : motor components, air intake systems,door handles, ..

High temperature 3D printing material PA6

KEY FEATURES & BENEFITS

Specifications of PA6-X028 by BASF:

  • Excellent thermal distorsion stability
  • High modulus and strength
  • Frictional and torque resistance
  • High burst resistance
  • Precise feature control

PA6-X028 by BASF TECHNICAL SPECIFICATION*

Bulk density
520 kg/m3 - DIN ISO 696
Average particle size - Diffraction laser
40 < " " < 110 μm
Average particle size - Grain size D10
40 μm
Average particle size - Grain size D50
70 μm
Average particle size - Grain size D90
110 μm
Printed part density - DIN EN ISO 1183-1
1140 kg/m3
Certification
Flammability according to: UL 94 HB: 2015 (<3mm) & Federal Motor Vehicle Safety Standard (FMVSS) No. 302
Melting temperature - ISO 11357
222°C
Crystallization temperature - ISO 11357
170°C
Melt volume flow rate - ISO 1133
18cm3/10 min
Melt viscosity - Rheometric
600 Pa s
HDT (at 1.8MPa) - ISO 75-2
99°C
Tensile strength - ISO 527-2
75 MPa
Tensile modulus - ISO 527-2
3750 MPa
Tensile elongation @ break - ISO 527-2
4.5 %
Flexural strength - ISO 178
110 MPa
Flexural Modulus - ISO 178
3200 MPa
Flexural elongation @ break - ISO 178
-- %
Impact Strength (notched) - ISO 179-2
3.0 kJ/m2
Impact Strength (unnotched) ISO 179-2
9 kJ/m2

Our compatible promaker printers

*mechanical properties measured after drying 2 days at 105 °C / vacuum and conditioned at 23°C / 50% r.H. for 7 days.

See also

PA12-S 1550
3D printing plastic powder