PA612-GB 3800

HIGH MODULUS IN TENSILE & FLEXURAL, WITH GOOD IMPACT RESISTANCE

The PA612-GB 3800 offers new possibilities for the series production of high performance functional parts requiring high rigidity combined with good impact resistance and thermal distortion stabililty for 3D printing in automotive and aerospace segments

PA612-GB-3800

KEY FEATURES & BENEFITS

AN IDEAL MATERIAL FOR MOTORSPORTS APPLICATION

Specifics feature of PA612-GB 3800:

  • Glass bead filled
  • High modulus in tensile & flexural, with good impact resistance
  • High resistance to thermal deformation
  • Easy to use powder even for large complex geometry or flat sided objects
  • Low sensitivity to moisture effects in processing and final use
  • Snap fit parts possible

Applications

Large parts for motorsports & automotive, aerospace and railway industries : fuel tanks, fuel circuits, air ducts, aerofoils, covers, pumps, casing, top parts of motors or ballast systems.

PA612-GB 3800 TECHNICAL SPECIFICATION

Average particle size
63 µm
Bulk Density
0.67 g/cm3
Density of parts
1.26 g/cm3
Moisture absorption
< 0.7 % (preliminary)
Melting Point
< 199 ° C +/ - 1°C
Heat Deflection 1.8 MPa
> 90°C (preliminary)
Tensile Strength
58 MPa +/- 5 MPa
Tensile Modulus
3800 MPa +/- 200MPa
Elongation @ break (XY)
6% +/- 3%
Elongation @ break (Z)
> 3%
Flexural Strength
90 MPa
Flexural Modulus
3600 MPa +/- 150Mpa
Impact Strength (unnotched Izod)
25 kJ/m2 (preliminary)
Shore Test
82 Shore D
Upper facing processed & blasting, Surface Ra
9 (preliminary)
Upper facing after Finishing, Surface Ra
2 (preliminary)
Upper facing after Finishing, Surface Ra
ISO
By
Powered by A. Schulman

See also

PA6-X028 by BASF
High temperature 3D printing material PA6
More
PA12-S 1550
3D printing plastic powder
More
PA12-GFX 2550
polymer-powder-3d-printing-pa12-gfx2550
More
Want to know more ?