STARK 3200

HIGH PERFORMANCE SELECTIVE LASER SINTERING MATERIAL

The new Stark 3200 is an high performance polymer insensitive to moisture, easy to machine, with a smooth surface finish and >3200 Young Modulus.

KEY FEATURES & BENEFITS

  • High performance isotropic properties
  • Not sensible to moisture
  • Smooth surfaces
  • Highly resistant to compression
  • Lightweight material

Typical applications:

  • Functional parts resistant to friction and wear under severe conditions (moisture, sliding on metal or ceramic parts).
  • Sealing under pressure and temperature: ducts, pipes, turbines, fittings
  • The final parts are easily machinable
  • Assembly by bonding possible

STARK 3200 TECHNICAL SPECIFICATION*

Appearance
Black
Average particle size
55 µm
Bulk Density
0.6 g/cm3
Density of parts
1.28g/cm3
Moisture absorption
0.25% (ISO 1110)
Melting Point
> 199 °C
Heat Deflection 1.8 MPa
> 75 °C
Tensile Strength
> 35 MPa
Tensile Modulus
> 3200 MPa
Elongation @ break
> 1.2%
Flexural Modulus
> 3000 MPa
Impact Strength (unnotched Izod)
> 14 KJ/m2
Shore Test
N.A.
A LARGE RANGE OF PREMIUM MATERIAL
  • Innovation and expertise
  • Quality control
  • Key partnerships
  • A wide range of possibilities

* Performance characteristics of these materials may change according to product application, operating conditions, material combined or end use

See also

PA11-GF 3450
More
PA6-X028 by BASF
High temperature 3D printing material PA6
More
PA612-GB 3800
More
Want to know more ?